SABIC Innovative Plastics LNP LUBRILOY D20001 PPO

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Lubriloy
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRILOY D20001 PPO.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRILOY* Z20001 is a compound based on PPO resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Flame Retardant.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Density 1.10 g/cc
0.0397 lb/in³
ASTM D792
Moisture Absorption 0.120 %
0.120 %
50% RH, 24 hrs; ASTM D570
0.220 %
0.220 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm

@Time 86400 sec
0.0080 - 0.010 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
0.010 - 0.030 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
Type I, 5 mm/min; ASTM D638
49.0 MPa
7110 psi
5 mm/min; ISO 527
Tensile Strength, Yield 57.0 MPa
8270 psi
Type I, 5 mm/min; ASTM D638
58.0 MPa
8410 psi
5 mm/min; ISO 527
Elongation at Break 24 %
24 %
5 mm/min; ISO 527
40 %
40 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 5.0 %
5.0 %
Type I, 5 mm/min; ASTM D638
5.0 %
5.0 %
5 mm/min; ISO 527
Tensile Modulus 2.00 GPa
290 ksi
1 mm/min; ISO 527
2.12 GPa
307 ksi
5 mm/min; ASTM D638
Flexural Strength 74.0 MPa
10700 psi
ISO 178
Flexural Modulus 1.92 GPa
278 ksi
2 mm/min; ISO 178
2.13 GPa
309 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 4.19 J/cm
7.85 ft-lb/in
ASTM D256
Izod Impact, Unnotched 21.1 J/cm
39.5 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 31.0 kJ/m²
14.8 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 210 kJ/m²
99.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 46.0 J

@Temperature 23.0 °C
33.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 45.0 J
33.2 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.27
0.27
ASTM D3702 Modified
Coefficient of Friction, Static 0.19
0.19
ASTM D3702 Modified
K (wear) Factor 109 x 10-8 mm³/N-M
54.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 87.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
48.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 98.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
54.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 116 °C
241 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
120 °C

@Thickness 3.20 mm
248 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 99.0 °C
210 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
105 °C

@Thickness 3.20 mm
221 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94