- SABIC Innovative Plastics LNP LUBRICOMP ZL003 PPE+PS
SABIC Innovative Plastics LNP LUBRICOMP ZL003 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP ZL003 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* ZL003 is a compound based on PPE+PS resin containing 15% PTFE. Added features of this material include: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0083 cm/cm @Time 86400 sec |
0.0083 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0087 cm/cm @Time 86400 sec |
0.0087 in/in @Time 24.0 hour |
ISO 294 |
| 0.0090 cm/cm @Time 86400 sec |
0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | ASTM D638 |
| 46.0 MPa | 6670 psi | ISO 527 | |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | ISO 527 |
| 47.0 MPa | 6820 psi | ASTM D638 | |
| Elongation at Break | 8.3 % | 8.3 % | ISO 527 |
| 8.9 % | 8.9 % | ASTM D638 | |
| Elongation at Yield | 8.1 % | 8.1 % | ISO 527 |
| 8.5 % | 8.5 % | ASTM D638 | |
| Tensile Modulus | 2.06 GPa | 299 ksi | 50 mm/min; ASTM D638 |
| 2.30 GPa | 334 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| 75.0 MPa | 10900 psi | ISO 178 | |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| 2.75 GPa | 399 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.67 J/cm | 5.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.28 | 0.28 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.20 | 0.20 | ASTM D3702 Modified |
| K (wear) Factor | 22.2 x 10-8 mm³/N-M | 11.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 119 °C | 246 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 117 °C @Thickness 3.20 mm |
243 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufFill™ 5008 Polyolefin
- Network Polymers NPP 30-1200 A
- Parker Chomerics Tecknit Consil®-II 841 Molded Silver-Filled Silicone Elastomer
- Fiberfil® PP-60/TC/15/VO/ND Polypropylene Homopolymer, 15% Talc Filled, Flame Retardant
- Lubriplate NO. 3 NO.3 Petroleum-Based Machine Tool Oil
- SGL Carbon Group EK 203 Graphite
- Hexcel® HexForce™ 1165 Fiber Glass Fabric
- Chosun Refractories ZR-C Special brick
- Axiall LSS-8200 Rigid PVC, Extrusion
- 3M FM157P Indoor UL Recognized Computer Imprintable Silver Polyester Label Product
Copyright © lookpolymers.com All Rights Reserved