SABIC Innovative Plastics LNP LUBRICOMP ZFL24 PPE+PS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP ZFL24 PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* ZFL24 is a compound based on PPE+PS resin containing 20% Glass Fiber, 10% PTFE. Added feature of this grade is: Wear Resistant.
Physical Properties Metric English Comments
Specific Gravity 1.29 g/cc
1.29 g/cc
ASTM D792
Density 1.29 g/cc
0.0466 lb/in³
ASTM D792
Moisture Absorption 0.0600 %
0.0600 %
50% RH, 24 hrs; ASTM D570
0.140 %
0.140 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm

@Time 86400 sec
0.0030 - 0.0060 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 - 0.0080 cm/cm

@Time 86400 sec
0.0050 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 92.0 MPa
13300 psi
5 mm/min; ISO 527
96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 1.9 %
1.9 %
5 mm/min; ISO 527
2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 7.12 GPa
1030 ksi
1 mm/min; ISO 527
7.54 GPa
1090 ksi
50 mm/min; ASTM D638
Flexural Strength 138 MPa
20000 psi
ISO 178
143 MPa
20700 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 144 MPa
20900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 6.57 GPa
953 ksi
2 mm/min; ISO 178
6.88 GPa
998 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.990 J/cm
1.85 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.69 J/cm
8.79 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 28.0 kJ/m²
13.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 10.0 J

@Temperature 23.0 °C
7.38 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.47
0.47
ASTM D3702 Modified
Coefficient of Friction, Static 0.54
0.54
ASTM D3702 Modified
K (wear) Factor 38.3 x 10-8 mm³/N-M
19.0 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D3702 Modified
203 x 10-8 mm³/N-M
101 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 72.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
40.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 56.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
31.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 136 °C
277 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
136 °C

@Thickness 3.20 mm
277 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 130 °C
266 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
131 °C

@Thickness 3.20 mm
268 °F

@Thickness 0.126 in
unannealed; ASTM D648