- SABIC Innovative Plastics LNP LUBRICOMP YL003C Polyester Elastomer
SABIC Innovative Plastics LNP LUBRICOMP YL003C Polyester Elastomer
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP YL003C Polyester Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LUBRICOMP* YL003C is a compound based on Polyester Elastomer resin containing 15% PTFE. Added features of this grade include: Clean Compound System, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 | |
| Water Absorption | 0.20 % @Time 173000 sec |
0.20 % @Time 48.0 hour |
ASTM D570 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.015 - 0.017 cm/cm @Time 86400 sec |
0.015 - 0.017 in/in @Time 24.0 hour |
ASTM D955 |
| 0.016 cm/cm @Time 86400 sec |
0.016 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.017 - 0.019 cm/cm @Time 86400 sec |
0.017 - 0.019 in/in @Time 24.0 hour |
ASTM D955 |
| 0.018 cm/cm @Time 86400 sec |
0.018 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 56 | 56 | ASTM D2240 |
| Tensile Strength at Break | 22.0 MPa | 3190 psi | ASTM D638 |
| Elongation at Break | 90 % | 90 % | ASTM D638 |
| >= 450 % | >= 450 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 0.260 GPa | 37.7 ksi | 1 mm/min; ISO 527 |
| 0.280 GPa | 40.6 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 12.0 MPa | 1740 psi | ISO 178 |
| 19.0 MPa | 2760 psi | ASTM D790 | |
| Flexural Modulus | 0.280 GPa | 40.6 ksi | ISO 178 |
| 0.290 GPa | 42.1 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.50 J/cm | 2.81 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.80 J/cm | 10.9 ft-lb/in | ASTM D4812 |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| 48.0 kJ/m² | 22.8 ft-lb/in² | 80*10*3; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 110 µm/m-°C @Temperature -40.0 - 40.0 °C |
61.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 110 µm/m-°C @Temperature -40.0 - 40.0 °C |
61.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 180 µm/m-°C @Temperature -40.0 - 40.0 °C |
100 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 180 µm/m-°C @Temperature -40.0 - 40.0 °C |
100 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 54.0 °C @Thickness 6.40 mm |
129 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.00 mm |
HB @Thickness 0.0394 in |
UL 94 |
Users viewing this material also viewed the following:
- PlastiComp Complet® LGF50 - PA6 Nylon 6, 50% Long Glass Fiber Reinforced
- Osprey Metals Oxygen-Free Electronic Copper Powder (Grade 80% - 22)
- Custom Resins Norpex® SE1 PPE (Polyphenylene Ether) (discontinued **)
- LyondellBasell Lupolen® 1840 D LDPE, Film Grade
- SABIC Innovative Plastics LNP STAT-KON AX00756 ABS
- Solvay Specialty Polymers Catalyst F/AC Polyolefin
- Special Metals NILO® Alloy 36 Low-Expansion Alloy
- A. Schulman POLYFORT™ FPP 2661 Injection Molding Grade Mineral Fortified Polypropylene
- Unifrax Fiberfrax® Durablanket® 2600 Ceramic Fiber Insulator
- Dow Corning DM6 Demulsifier
Copyright © lookpolymers.com All Rights Reserved