SABIC Innovative Plastics LNP LUBRICOMP XFL21R PA
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP XFL21R PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* XFL21R is a compound based on Amorphous Nylon resin containing 5% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Mold Release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 84.0 MPa | 12200 psi | ASTM D638 |
| Elongation at Break | 4.1 % | 4.1 % | ASTM D638 |
| Tensile Modulus | 3.73 GPa | 541 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 3.90 GPa | 566 ksi | ASTM D790 |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.06 J/cm | 9.48 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |