SABIC Innovative Plastics LNP LUBRICOMP WL002 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP WL002 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP WL002 is a compound based on PBT resin containing 10% PTFE. Added feature of this grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0900 % | 0.0900 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.0 MPa | 7400 psi | Type I, 5 mm/min; ASTM D638 |
| 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 |
| 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 10.9 % | 10.9 % | 5 mm/min; ISO 527 |
| 12 % | 12 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 9.3 % | 9.3 % | Type I, 5 mm/min; ASTM D638 |
| 9.8 % | 9.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.78 GPa | 403 ksi | 50 mm/min; ASTM D638 |
| 2.90 GPa | 421 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 78.0 MPa | 11300 psi | ISO 178 |
| Flexural Modulus | 2.34 GPa | 339 ksi | 2 mm/min; ISO 178 |
| 2.64 GPa | 383 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.390 J/cm | 0.731 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.80 J/cm | 16.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 53.0 kJ/m² | 25.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.35 | 0.35 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.31 | 0.31 | ASTM D3702 Modified |
| K (wear) Factor | 4.03 x 10-8 mm³/N-M | 2.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 50.4 x 10-8 mm³/N-M | 25.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 97.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
54.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 98.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
54.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 182 °C @Thickness 3.20 mm |
360 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.0 °C | 135 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 58.0 °C @Thickness 3.20 mm |
136 °F @Thickness 0.126 in |
unannealed; ASTM D648 |