SABIC Innovative Plastics LNP LUBRICOMP WFL34 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP WFL34 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* WFL34 is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
Physical Properties Metric English Comments
Density 1.58 g/cc
0.0571 lb/in³
ASTM D792
1.58 g/cc
0.0571 lb/in³
ISO 1183
Moisture Absorption 0.0500 %
0.0500 %
50% RH, 24 hrs; ASTM D570
0.0700 %
0.0700 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
0.010 - 0.030 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 114 MPa
16500 psi
5 mm/min; ISO 527
118 MPa
17100 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 114 MPa
16500 psi
5 mm/min; ISO 527
118 MPa
17100 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.5 %
2.5 %
5 mm/min; ISO 527
2.6 %
2.6 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.5 %
2.5 %
5 mm/min; ISO 527
2.6 %
2.6 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 7.88 GPa
1140 ksi
1 mm/min; ISO 527
8.27 GPa
1200 ksi
50 mm/min; ASTM D638
Flexural Strength 173 MPa
25100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 173 MPa
25100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 7.06 GPa
1020 ksi
2 mm/min; ISO 178
7.48 GPa
1080 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.83 J/cm
12.8 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 41.0 kJ/m²
19.5 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 7.00 J

@Temperature 23.0 °C
5.16 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.24
0.24
ASTM D3702 Modified
Coefficient of Friction, Static 0.22
0.22
ASTM D3702 Modified
K (wear) Factor 88.6 x 10-8 mm³/N-M
44.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 36.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
20.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 89.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
49.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 222 °C
432 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
222 °C

@Thickness 3.20 mm
432 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 208 °C
406 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
210 °C

@Thickness 3.20 mm
410 °F

@Thickness 0.126 in
unannealed; ASTM D648