SABIC Innovative Plastics LNP LUBRICOMP WFL33 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP WFL33 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* WFL33 is a compound based on PBT containing 15% Glass Fiber, 15% PTFE. Added feature of this grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 |
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 |
| 87.0 MPa | 12600 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.9 % | 2.9 % | Type I, 5 mm/min; ASTM D638 |
| 3.1 % | 3.1 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.19 GPa | 898 ksi | 1 mm/min; ISO 527 |
| 6.35 GPa | 921 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 145 MPa | 21000 psi | ISO 178 |
| 149 MPa | 21600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 150 MPa | 21800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.51 GPa | 799 ksi | 2 mm/min; ISO 178 |
| 5.70 GPa | 827 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.620 J/cm | 1.16 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.98 J/cm | 11.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 38.0 kJ/m² | 18.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.44 | 0.44 | ASTM D3702 Modified |
| K (wear) Factor | 8.06 x 10-8 mm³/N-M | 4.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 107 x 10-8 mm³/N-M | 53.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 44.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
24.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 118 µm/m-°C @Temperature -30.0 - 30.0 °C |
65.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 222 °C @Thickness 3.20 mm |
432 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 |