SABIC Innovative Plastics LNP LUBRICOMP WAL34 PBT

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP WAL34 PBT.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* WAL34 is a compound based on (PBT resin containing 15% PTFE, 20% Aramid Fiber. Added features of this material include: Wesr Resistant.

Physical Properties	Metric	English	Comments
Specific Gravity	1.43 g/cc	1.43 g/cc	ASTM D792
Density	1.42 g/cc	0.0513 lb/inÂ³	ASTM D792
Moisture Absorption	0.0900 %	0.0900 %	50% RH, 24 hrs; ASTM D570
	0.0900 %	0.0900 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.013 cm/cm @Time 86400 sec	0.013 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.022 cm/cm @Time 86400 sec	0.022 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	44.0 MPa	6380 psi	5 mm/min; ISO 527
	46.0 MPa	6670 psi	Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield	44.0 MPa	6380 psi	5 mm/min; ISO 527
	46.0 MPa	6670 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	1.3 %	1.3 %	5 mm/min; ISO 527
	1.5 %	1.5 %	Type I, 5 mm/min; ASTM D638
Elongation at Yield	1.3 %	1.3 %	5 mm/min; ISO 527
	1.5 %	1.5 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	4.52 GPa	656 ksi	1 mm/min; ISO 527
	5.48 GPa	795 ksi	50 mm/min; ASTM D638
Flexural Strength	78.0 MPa	11300 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength	78.0 MPa	11300 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	4.10 GPa	595 ksi	2 mm/min; ISO 178
	4.39 GPa	637 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	0.320 J/cm	0.599 ft-lb/in	ASTM D256
Izod Impact, Unnotched	1.31 J/cm	2.45 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	3.00 kJ/mÂ²	1.43 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	9.00 kJ/mÂ²	4.28 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	3.00 J @Temperature 23.0 Â°C	2.21 ft-lb @Temperature 73.4 Â°F	ASTM D3763
Coefficient of Friction, Dynamic	0.24	0.24	ASTM D3702 Modified
Coefficient of Friction, Static	0.21	0.21	ASTM D3702 Modified
K (wear) Factor	12.1 x 10^-8 mmÂ³/N-M	6.00 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	51.0 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	28.3 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
CTE, linear, Transverse to Flow	84.0 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	46.7 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	206 Â°C	403 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	215 Â°C @Thickness 6.40 mm	419 Â°F @Thickness 0.252 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	130 Â°C	266 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	182 Â°C @Thickness 3.20 mm	360 Â°F @Thickness 0.126 in	unannealed; ASTM D648