SABIC Innovative Plastics LNP LUBRICOMP VN001 Super Tough Nylon

Category Polymer , Thermoplastic , Nylon
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP VN001 Super Tough Nylon.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* VN001 is a compound based on Super Tough Nylon containing 2% MOS2. Added feature of th is grade is: Wear Resistant.
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
ASTM D792
1.10 g/cc
0.0397 lb/in³
ISO 1183
Moisture Absorption 0.800 %
0.800 %
50% RH, 24 hrs; ASTM D570
1.10 %
1.10 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow >= 0.020 cm/cm

@Time 86400 sec
>= 0.020 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.020 - 0.050 cm/cm

@Time 86400 sec
0.020 - 0.050 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
Type I, 5 mm/min; ASTM D638
53.0 MPa
7690 psi
5 mm/min; ISO 527
Tensile Strength, Yield 53.0 MPa
7690 psi
Type I, 5 mm/min; ASTM D638
56.0 MPa
8120 psi
5 mm/min; ISO 527
Elongation at Break 4.0 %
4.0 %
Flexural Strain, break, 2 mm/min; ISO 178
28 %
28 %
5 mm/min; ISO 527
40.6 %
40.6 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 5.2 %
5.2 %
5 mm/min; ISO 527
38 %
38 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.29 GPa
332 ksi
50 mm/min; ASTM D638
2.38 GPa
345 ksi
1 mm/min; ISO 527
Flexural Yield Strength 69.0 MPa
10000 psi
2 mm/min; ISO 178
Flexural Modulus 1.91 GPa
277 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.08 GPa
302 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.58 J/cm
2.96 ft-lb/in
ASTM D256
Izod Impact, Unnotched 17.3 J/cm
32.4 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 182 kJ/m²
86.6 ft-lb/in²
80*10*4; ISO 180/1U
Impact Test 22.0 J
16.2 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.79
0.79
ASTM D3702 Modified
Coefficient of Friction, Static 0.36
0.36
ASTM D3702 Modified
K (wear) Factor 143 x 10-8 mm³/N-M
71.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 118 µm/m-°C

@Temperature -30.0 - 30.0 °C
65.6 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 118 µm/m-°C

@Temperature -30.0 - 30.0 °C
65.6 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
216 °C

@Thickness 3.20 mm
421 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 64.0 °C
147 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
65.0 °C

@Thickness 3.20 mm
149 °F

@Thickness 0.126 in
unannealed; ASTM D648