SABIC Innovative Plastics LNP LUBRICOMP RX06480 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP RX06480 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* RX06480 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 15% Lubricants. Added feature of this material is: Wear Resistant.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
ISO 1183
1.50 g/cc
0.0542 lb/in³
ASTM D792
Moisture Absorption 0.500 %
0.500 %
50% RH, 24 hrs; ASTM D570
0.740 %
0.740 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Time 86400 sec
 0.0040 - 0.0060 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm

@Time 86400 sec
 0.0070 - 0.0090 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 162 MPa
23500 psi
5 mm/min; ISO 527
163 MPa
23600 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 162 MPa
23500 psi
5 mm/min; ISO 527
163 MPa
23600 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.1 %
2.1 %
Type I, 5 mm/min; ASTM D638
2.1 %
2.1 %
5 mm/min; ISO 527
Elongation at Yield 2.1 %
2.1 %
Type I, 5 mm/min; ASTM D638
2.1 %
2.1 %
5 mm/min; ISO 527
Tensile Modulus 11.21 GPa
1626 ksi
1 mm/min; ISO 527
12.12 GPa
1758 ksi
50 mm/min; ASTM D638
Flexural Strength 229 MPa
33200 psi
1.3 mm/min, 50 mm span; ASTM D790
230 MPa
33400 psi
ISO 178
Flexural Yield Strength 229 MPa
33200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 9.82 GPa
1420 ksi
1.3 mm/min, 50 mm span; ASTM D790
9.91 GPa
1440 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.940 J/cm
1.76 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.45 J/cm
14.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 46.0 kJ/m²
21.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 10.0 J

@Temperature 23.0 °C
 7.38 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.56
0.56
ASTM D3702 Modified
Coefficient of Friction, Static 0.44
0.44
ASTM D3702 Modified
K (wear) Factor 4.03 x 10-8 mm³/N-M
2.00 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D3702 Modified
48.3 x 10-8 mm³/N-M
24.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 27.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 15.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
CTE, linear, Transverse to Flow 57.6 µm/m-°C

@Temperature -30.0 - 30.0 °C
 32.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
260 °C

@Thickness 3.20 mm
 500 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 247 °C
477 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
252 °C

@Thickness 3.20 mm
 486 °F

@Thickness 0.126 in
 unannealed; ASTM D648