SABIC Innovative Plastics LNP LUBRICOMP RP004S PA 66

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP RP004S PA 66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* RP004S is a compound based on Nylon 66 containing PTFE/Silicone. Added features of this grade include: Heat Stabilized, Wear Resistant.

Physical Properties	Metric	English	Comments
Specific Gravity	1.24 g/cc	1.24 g/cc	ASTM D792
Density	1.24 g/cc	0.0448 lb/inÂ³	ISO 1183
Moisture Absorption	0.860 %	0.860 %	50% RH, 24 hrs; ASTM D570
	1.20 %	1.20 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	>= 0.020 cm/cm @Time 86400 sec	>= 0.020 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.010 - 0.030 cm/cm @Time 86400 sec	0.010 - 0.030 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	59.0 MPa	8560 psi	Type I, 5 mm/min; ASTM D638
	64.0 MPa	9280 psi	5 mm/min; ISO 527
Tensile Strength, Yield	61.0 MPa	8850 psi	Type I, 5 mm/min; ASTM D638
	65.0 MPa	9430 psi	5 mm/min; ISO 527
Elongation at Break	18 %	18 %	Type I, 5 mm/min; ASTM D638
	19 %	19 %	5 mm/min; ISO 527
Elongation at Yield	4.8 %	4.8 %	Type I, 5 mm/min; ASTM D638
	4.8 %	4.8 %	5 mm/min; ISO 527
Tensile Modulus	2.75 GPa	399 ksi	1 mm/min; ISO 527
	2.95 GPa	428 ksi	50 mm/min; ASTM D638
Flexural Strength	78.0 MPa	11300 psi	ISO 178
Flexural Modulus	2.15 GPa	312 ksi	1.3 mm/min, 50 mm span; ASTM D790
	2.22 GPa	322 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.460 J/cm	0.862 ft-lb/in	ASTM D256
Izod Impact, Unnotched	13.6 J/cm	25.5 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	5.00 kJ/mÂ²	2.38 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	115 kJ/mÂ²	54.7 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	3.00 J @Temperature 23.0 Â°C	2.21 ft-lb @Temperature 73.4 Â°F	ASTM D3763
Impact Test	2.00 J	1.48 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.23	0.23	ASTM D3702 Modified
Coefficient of Friction, Static	0.11	0.11	ASTM D3702 Modified
K (wear) Factor	8.06 x 10^-8 mmÂ³/N-M	4.00 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	115 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	63.9 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
CTE, linear, Transverse to Flow	113 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	62.8 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	154 Â°C	309 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	184 Â°C @Thickness 3.20 mm	363 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	57.0 Â°C	135 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	57.0 Â°C @Thickness 3.20 mm	135 Â°F @Thickness 0.126 in	unannealed; ASTM D648