- SABIC Innovative Plastics LNP LUBRICOMP RP003 PA 66
SABIC Innovative Plastics LNP LUBRICOMP RP003 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RP003 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RP003 is a compound based on Nylon 66 resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.600 % | 0.600 % | 50% RH, 24 hrs; ASTM D570 |
| 0.970 % | 0.970 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7110 psi | Type I, 5 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | Type I, 5 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 4.7 % | 4.7 % | Type I, 5 mm/min; ASTM D638 |
| 4.7 % | 4.7 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.6 % | 4.6 % | Type I, 5 mm/min; ASTM D638 |
| 4.8 % | 4.8 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.69 GPa | 390 ksi | 50 mm/min; ASTM D638 |
| 2.96 GPa | 429 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 73.0 MPa | 10600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 73.0 MPa | 10600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.26 GPa | 328 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.58 GPa | 374 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.79 J/cm | 7.10 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 1.00 J | 0.738 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.22 | 0.22 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.16 | 0.16 | ASTM D3702 Modified |
| K (wear) Factor | 20.1 x 10-8 mm³/N-M | 10.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 91.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 95.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 96.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
53.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 201 °C @Thickness 3.20 mm |
394 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 59.0 °C @Thickness 3.20 mm |
138 °F @Thickness 0.126 in |
unannealed; ASTM D648 |