SABIC Innovative Plastics LNP LUBRICOMP RFG16 PA 66 (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP RFG16 PA 66 (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* RFG16 is a compound based on PA 66 resin containing Glass Fiber, Graphite. Added features include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0024 cm/cm
0.0024 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 156 MPa
22600 psi
5 mm/min; ISO 527
Elongation at Break 2.2 %
2.2 %
5 mm/min; ISO 527
3.8 %
3.8 %
Flexural Strain, break, 2 mm/min; ISO 178
Tensile Modulus 9.80 GPa
1420 ksi
1 mm/min; ISO 527
Flexural Strength 249 MPa
36100 psi
2 mm/min; ISO 178
Flexural Yield Strength 249 MPa
36100 psi
2 mm/min; ISO 178
Flexural Modulus 8.70 GPa
1260 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 60.0 kJ/m²
28.6 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 26.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 14.4 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 89.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 49.4 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2