SABIC Innovative Plastics LNP LUBRICOMP RCP36 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP RCP36 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* RCP36 is a compound based on Nylon 66 resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear Resistant.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ASTM D792
1.34 g/cc
0.0484 lb/in³
ISO 1183
Moisture Absorption 0.930 %
0.930 %
50% RH, 24 hrs; ASTM D570
1.35 %
1.35 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0015 cm/cm

@Time 86400 sec
0.0015 in/in

@Time 24.0 hour
ISO 294
0.0020 cm/cm

@Time 86400 sec
0.0020 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0040 cm/cm

@Time 86400 sec
0.0040 in/in

@Time 24.0 hour
ASTM D955
0.0043 cm/cm

@Time 86400 sec
0.0043 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 201 MPa
29200 psi
ASTM D638
228 MPa
33100 psi
ISO 527
Elongation at Break 1.4 %
1.4 %
ASTM D638
2.0 %
2.0 %
ISO 527
Tensile Modulus 23.1 GPa
3350 ksi
1 mm/min; ISO 527
29.5 GPa
4280 ksi
50 mm/min; ASTM D638
Flexural Strength 333 MPa
48300 psi
ASTM D790
354 MPa
51300 psi
ISO 178
Flexural Modulus 16.4 GPa
2380 ksi
ASTM D790
21.3 GPa
3090 ksi
ISO 178
Izod Impact, Notched 0.960 J/cm
1.80 ft-lb/in
ASTM D256
Izod Impact, Unnotched 9.45 J/cm
17.7 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 65.0 kJ/m²
30.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 9.00 J
6.64 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.25
0.25
ASTM D3702 Modified
Coefficient of Friction, Static 0.22
0.22
ASTM D3702 Modified
K (wear) Factor 12.1 x 10-8 mm³/N-M
6.00 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 21.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
12.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
22.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
12.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 34.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
19.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
34.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
19.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 254 °C

@Thickness 3.20 mm
489 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
244 °C

@Thickness 3.20 mm
471 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94 by SABIC-IP