SABIC Innovative Plastics LNP LUBRICOMP QCP36 PA6.10

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP QCP36 PA6.10.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* QCP36 is a compound based on Nylon 6/10 resin containing 15% PTFE/Silicone, 30% Carbon Fiber. Added features of this material include: Wear Resistant. Electrically Conductive
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ASTM D792
1.32 g/cc
0.0477 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0035 cm/cm

@Time 86400 sec
0.0035 in/in

@Time 24.0 hour
ISO 294
0.0040 cm/cm

@Time 86400 sec
0.0040 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ASTM D955
0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 173 MPa
25100 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 173 MPa
25100 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 1.9 %
1.9 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 19.2 GPa
2780 ksi
1 mm/min; ISO 527
19.85 GPa
2879 ksi
50 mm/min; ASTM D638
Flexural Strength 282 MPa
40900 psi
ASTM D790
Flexural Modulus 16.54 GPa
2399 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 8.01 J/cm
15.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 49.0 kJ/m²
23.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 6.00 J
4.43 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.46
0.46
ASTM D3702 Modified
Coefficient of Friction, Static 0.46
0.46
ASTM D3702 Modified
K (wear) Factor 30.2 x 10-8 mm³/N-M
15.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 48.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
48.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 25.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
14.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
26.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
14.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 222 °C
432 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
221 °C

@Thickness 3.20 mm
430 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 212 °C
414 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
212 °C

@Thickness 3.20 mm
414 °F

@Thickness 0.126 in
unannealed; ASTM D648