SABIC Innovative Plastics LNP LUBRICOMP QAP22S PA 6/10 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP QAP22S PA 6/10 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* QAP22S is a compound based on Nylon 6/10 resin containing PTFE, Aramid Fiber, Silicone. Added features of this material include: Internally Lubricated, Heat Stabilized.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ASTM D792
1.17 g/cc
0.0423 lb/in³
ISO 1183
Moisture Absorption 0.300 %
0.300 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.010 cm/cm

@Time 86400 sec
0.010 in/in

@Time 24.0 hour
ASTM D955
0.010 cm/cm

@Time 86400 sec
0.010 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.018 cm/cm

@Time 86400 sec
0.018 in/in

@Time 24.0 hour
ASTM D955
0.018 cm/cm

@Time 86400 sec
0.018 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
ASTM D638
50.0 MPa
7250 psi
ISO 527
Tensile Strength, Yield 45.0 MPa
6530 psi
ASTM D638
50.0 MPa
7250 psi
ISO 527
Elongation at Break 1.8 %
1.8 %
ASTM D638
2.3 %
2.3 %
ISO 527
Elongation at Yield 1.8 %
1.8 %
ASTM D638
2.3 %
2.3 %
ISO 527
Tensile Modulus 3.31 GPa
480 ksi
1 mm/min; ISO 527
3.44 GPa
499 ksi
50 mm/min; ASTM D638
Flexural Strength 76.0 MPa
11000 psi
ISO 178
103 MPa
14900 psi
ASTM D790
Flexural Modulus 2.75 GPa
399 ksi
ASTM D790
3.00 GPa
435 ksi
ISO 178
Izod Impact, Notched 0.370 J/cm
0.693 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.52 J/cm
6.59 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 32.0 kJ/m²
15.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 1.00 J
0.738 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.41
0.41
ASTM D3702 Modified
Coefficient of Friction, Static 0.26
0.26
ASTM D3702 Modified
K (wear) Factor 22.2 x 10-8 mm³/N-M
11.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 84.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
84.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
47.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 63.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
63.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 193 °C
379 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
203 °C

@Thickness 3.20 mm
397 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 94.0 °C
201 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
118 °C

@Thickness 3.20 mm
244 °F

@Thickness 0.126 in
unannealed; ASTM D648