- SABIC Innovative Plastics LNP LUBRICOMP Noryl_NWR5810 PPE+HIPS (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP LUBRICOMP Noryl_NWR5810 PPE+HIPS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP Noryl_NWR5810 PPE+HIPS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* Noryl_NWR5810 compound is a 10% PTFE filled PPE+PS. High flow and good impact. Applications requiring wear resistance/lubricity. Electronics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0055 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0055 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0045 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0045 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 5.5 g/10 min @Load 5.00 kg, Temperature 260 °C |
5.5 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 37.0 MPa | 5370 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 55 % | 55 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 2.8 % | 2.8 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.17 GPa | 315 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 57.0 MPa | 8270 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 61.0 MPa | 8850 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 1.99 GPa | 289 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 2.06 GPa | 299 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 2.32 J/cm | 4.35 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 22.42 J/cm | 42.00 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 32.0 J @Temperature 23.0 °C |
23.6 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.8 µm/m-°C @Temperature -40.0 - 60.0 °C |
36.0 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 73.8 µm/m-°C @Temperature -40.0 - 60.0 °C |
41.0 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C @Thickness 3.20 mm |
235 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 116 °C @Thickness 6.40 mm |
241 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 105 °C @Thickness 6.40 mm |
221 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 110 °C | 230 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Nylene® PA6 Homopolymer 201 Nylon 6; Low Viscosity Nucleated
- Polymer Resources NY66-IM2-LM Nylon, Preliminary Data Sheet, Low Flexural Modulus, High Impact (DAM)
- NOVA Chemicals Novapol® LF-0219-A LDPE Blow Molding Resin
- DuPont Performance Polymers Crastin® S610SF BK851 PBT (Unverified Data**)
- Polykemi AB POLYfill PPH T15010 H VTUV1 Polypropylene Homopolymer, Mineral Reinforced
- ICO Polymers ICORENEâ„¢ 115-1323 LMDPE Rotational Molding Resin
- Chevron Phillips MarFlex® 7109 LLDPE Blown Film Resin
- 3M Scotchcal™ ElectroCut™ 7725-12 Graphic Film
- SABIC Innovative Plastics ULTEM 1000 PEI (Europe-Africa-Middle East)
- Westlake Mxsten CV77526 Polyethylene Plastomer
Copyright © lookpolymers.com All Rights Reserved