SABIC Innovative Plastics LNP LUBRICOMP NL001 PC+ABS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP NL001 PC+ABS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* NL001 is a wear resistant PC+ABS blend, suitable for thin wall applications.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ASTM D792
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 26 g/10 min

@Load 5.00 kg,
Temperature 260 °C
26 g/10 min

@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
5 mm/min; ISO 527
40.0 MPa
5800 psi
50 mm/min; ISO 527
43.0 MPa
6240 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 45.0 MPa
6530 psi
5 mm/min; ISO 527
50.0 MPa
7250 psi
50 mm/min; ISO 527
53.0 MPa
7690 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 20 %
20 %
50 mm/min; ISO 527
24.3 %
24.3 %
Type I, 50 mm/min; ASTM D638
45 %
45 %
5 mm/min; ISO 527
Elongation at Yield 3.6 %
3.6 %
Type I, 50 mm/min; ASTM D638
4.0 %
4.0 %
5 mm/min; ISO 527
4.0 %
4.0 %
50 mm/min; ISO 527
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527
2.40 GPa
348 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 80.0 MPa
11600 psi
2 mm/min; ISO 178
86.0 MPa
12500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.44 GPa
354 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.50 GPa
363 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 87.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
48.3 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Hot Ball Pressure Test <= 100 °C
<= 212 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 114 °C
237 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
116 °C

@Thickness 3.20 mm
241 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
99.0 °C

@Thickness 3.20 mm
210 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 113 °C
235 °F
Rate B/50; ISO 306
115 °C
239 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
UL 94 by SABIC-IP
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
UL 94 by SABIC-IP
Oxygen Index 21 %
21 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASSES
IEC 60695-10-2