SABIC Innovative Plastics LNP LUBRICOMP ML008 PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP ML008 PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* ML008 is a compound based on Polypropylene resin containing PTFE. Added Features include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 19.6 % | 19.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 1.30 GPa | 189 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 40.0 MPa | 5800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.60 GPa | 232 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 128 µm/m-°C @Temperature 23.0 - 60.0 °C |
71.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 135 µm/m-°C @Temperature 23.0 - 60.0 °C |
75.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Nilit Nilitop BT N Unfilled, Nucleated PBT
- SABIC Innovative Plastics Geloy FXTW30CP ASA
- Lord Adhesives 26 No-Mix Accelerator for 200/500 Series
- Isoflon PTFE + 60% Bronze Polytetrafluoroethylene with 60% Bronze
- LyondellBasell Alathon® L5005V High Density Polyethylene, HMW Film Grade
- DSM Stanyl® TW241F8 Nylon 46-40% Glass Reinforced, Heat Stabilized, Lubricated (Asian Grade) (Cond)
- Epoxy Technology EPO-TEK® OE188 High Temperature Silica-Filled Epoxy
- DuPont Performance Polymers Zytel® RS 30G30L NC010 Nylon 610
- ATI Allvac® Vasco® 17-4 Precipitation Hardening Steel, Heat Treatment: 1038°C (1900°F) + Age
- BASF Cyclohexylamine (CHA)
Copyright © lookpolymers.com All Rights Reserved