SABIC Innovative Plastics LNP LUBRICOMP ML004S PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP ML004S PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* ML004S is a compound based on Polypropylene resin containing 20% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 29.0 MPa | 4210 psi | 5 mm/min; ISO 527 |
| 30.0 MPa | 4350 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 5 mm/min; ISO 527 |
| 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 13 % | 13 % | 5 mm/min; ISO 527 |
| 15 % | 15 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| 5.6 % | 5.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.66 GPa | 241 ksi | 1 mm/min; ISO 527 |
| 2.02 GPa | 293 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 44.0 MPa | 6380 psi | ISO 178 |
| Flexural Yield Strength | 47.0 MPa | 6820 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.69 GPa | 245 ksi | 2 mm/min; ISO 178 |
| 1.76 GPa | 255 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.440 J/cm | 0.824 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.48 J/cm | 6.52 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 22.0 kJ/m² | 10.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.77 | 0.77 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.62 | 0.62 | ASTM D3702 Modified |
| K (wear) Factor | 12.1 x 10-8 mm³/N-M | 6.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 346 x 10-8 mm³/N-M | 172 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 91.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
50.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 39.8 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 119 °C @Thickness 3.20 mm |
246 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 65.0 °C @Thickness 3.20 mm |
149 °F @Thickness 0.126 in |
unannealed; ASTM D648 |