SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR6300 AES+PC+SAN (Asia Pacific)

Category Polymer , Thermoplastic , AES Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR6300 AES+PC+SAN (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Wear resistant PC+SAN, with proprietary lubricant, for business equipment applications.
Physical Properties Metric English Comments
Specific Gravity 1.17 g/cc
1.17 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Index of Compound 38 g/10 min

@Load 2.16 kg,
Temperature 300 °C
38 g/10 min

@Load 4.76 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 61.0 MPa
8850 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 164 %
164 %
Type I, 50 mm/min; ASTM D638
Flexural Yield Strength 96.0 MPa
13900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.48 GPa
360 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 6.78 J/cm
12.7 ft-lb/in
ASTM D256
1.65 J/cm

@Temperature -30.0 °C
3.09 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 25.31 J/cm
47.42 ft-lb/in
ASTM D4812
Dart Drop, Total Energy 60.0 J

@Temperature 23.0 °C
44.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 106 µm/m-°C

@Temperature -40.0 - 40.0 °C
58.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 119 µm/m-°C

@Temperature -40.0 - 40.0 °C
66.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 133 °C

@Thickness 6.40 mm
271 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 117 °C

@Thickness 3.20 mm
243 °F

@Thickness 0.126 in
unannealed; ASTM D648
121 °C

@Thickness 6.40 mm
250 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 136 °C
277 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 80.0 °C
176 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.49 mm
HB

@Thickness 0.0587 in
UL 94