SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1520A PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1520A PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% glass reinforced/15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0015 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0045 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0045 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 93.0 MPa | 13500 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 93.0 MPa | 13500 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 148 MPa | 21500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 6.20 GPa | 899 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 17.0 J @Temperature 23.0 °C |
12.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 52.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 133 °C @Thickness 3.20 mm |
271 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.49 mm |
V-0 @Thickness 0.0587 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Nye Lubricants 737B (RL) Synthetic Oil
- PolyOne Syncure™ System S107FH Polyethylene, Crosslinked (XLPE)
- Rogers Corporation Poron® 4701-41-20 Urethane Foam, Soft, Enhanced Sealability
- Zeon Chemicals Hydrin® T3000LL Polyepichlorohydrin Elastomer
- Chosun Refractories L15HU Magnesia Carbon Bricks for Ladle Slag Line
- Fainplast Compounds PMS 75 Flexible PVC, Lead Free
- Alliance Polymers Viprene™ G40D-22U-NAT Thermoplastic Vulcanizate Elastomer
- Carpenter AerMet® 100 Aged at 875°F
- Fainplast Compounds RE 130 Rigid PVC, Extrusion
- SABIC Innovative Plastics LNP STAT-KON RCL42 PA 66 (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved