SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1510A PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1510A PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* Lexan_LF1510A compound is a 10% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0035 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0035 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.1 g/10 min @Load 1.20 kg, Temperature 300 °C |
8.1 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.79 GPa | 550 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.07 J/cm | 9.50 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.49 mm |
V-0 @Thickness 0.0587 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |