SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP LL004C PEEK.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* LL004C is a compound based on Polyetheretherketone resin containing 20% PTFE. Added features of this material include: Wear Resistant, Clean Compounding System.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ASTM D792
1.37 g/cc
0.0495 lb/in³
ISO 1183
Moisture Absorption 0.0600 %
0.0600 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.013 cm/cm

@Time 86400 sec
0.013 in/in

@Time 24.0 hour
ASTM D955
0.013 cm/cm

@Time 86400 sec
0.013 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0185 cm/cm

@Time 86400 sec
0.0185 in/in

@Time 24.0 hour
ISO 294
0.019 cm/cm

@Time 86400 sec
0.019 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 69.0 MPa
10000 psi
ASTM D638
69.0 MPa
10000 psi
ISO 527
Tensile Strength, Yield 73.0 MPa
10600 psi
ISO 527
74.0 MPa
10700 psi
ASTM D638
Elongation at Break 11.8 %
11.8 %
ISO 527
23.3 %
23.3 %
ASTM D638
Elongation at Yield 5.0 %
5.0 %
ISO 527
5.8 %
5.8 %
ASTM D638
Tensile Modulus 2.89 GPa
419 ksi
50 mm/min; ASTM D638
3.06 GPa
444 ksi
1 mm/min; ISO 527
Flexural Strength 117 MPa
17000 psi
ASTM D790
118 MPa
17100 psi
ISO 178
Flexural Modulus 2.96 GPa
429 ksi
ASTM D790
3.32 GPa
482 ksi
ISO 178
Izod Impact, Notched 0.960 J/cm
1.80 ft-lb/in
ASTM D256
Izod Impact, Unnotched 15.48 J/cm
29.00 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 91.0 kJ/m²
43.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 3.00 J
2.21 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.52
0.52
ASTM D3702 Modified
Coefficient of Friction, Static 0.43
0.43
ASTM D3702 Modified
K (wear) Factor 258 x 10-8 mm³/N-M
128 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified