SABIC Innovative Plastics LNP LUBRICOMP LCL33E PEEK

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP LCL33E PEEK.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* LCL33E is a compound based on Polyetheretherketone resin containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Easy Molding, Wear Resistant.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ASTM D792
1.43 g/cc
0.0517 lb/in³
ISO 1183
Moisture Absorption 0.0700 %
0.0700 %
50% RH, 24 hrs; ASTM D570
0.700 %
0.700 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D955
0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0030 - 0.0070 cm/cm

@Time 86400 sec
0.0030 - 0.0070 in/in

@Time 24.0 hour
ISO 294
0.0040 - 0.0070 cm/cm

@Time 86400 sec
0.0040 - 0.0070 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 179 MPa
26000 psi
ASTM D638
187 MPa
27100 psi
ISO 527
Elongation at Break 1.6 %
1.6 %
ISO 527
1.7 %
1.7 %
ASTM D638
Tensile Modulus 14.7 GPa
2130 ksi
1 mm/min; ISO 527
16.61 GPa
2409 ksi
50 mm/min; ASTM D638
Flexural Strength 266 MPa
38600 psi
ASTM D790
275 MPa
39900 psi
ISO 178
Flexural Modulus 12.96 GPa
1880 ksi
ASTM D790
14.7 GPa
2130 ksi
ISO 178
Izod Impact, Notched 0.640 J/cm
1.20 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.91 J/cm
9.20 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 34.0 kJ/m²
16.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 8.00 J
5.90 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Coefficient of Friction, Dynamic 0.35
0.35
ASTM D3702 Modified
Coefficient of Friction, Static 0.28
0.28
ASTM D3702 Modified
K (wear) Factor 26.2 x 10-8 mm³/N-M
13.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 23.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
13.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
23.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
13.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 41.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
23.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
41.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
23.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) >= 240 °C
>= 464 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
>= 298 °C

@Thickness 3.20 mm
>= 568 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP