SABIC Innovative Plastics LNP LUBRICOMP KX06415 Acetal Copolymer

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP KX06415 Acetal Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* KX06415 is a compound based on Acetal Copolymer resin containing 10% PTFE, 10% Aramid Powder. Added features of this material include: Easy Molding, Heat Stabilized, Wear Resistant.
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
ASTM D792
Density 1.45 g/cc
0.0524 lb/in³
ASTM D792
Moisture Absorption 0.210 %
0.210 %
50% RH, 24 hrs; ASTM D570
0.350 %
0.350 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow >= 0.020 cm/cm

@Time 86400 sec
>= 0.020 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.020 - 0.040 cm/cm

@Time 86400 sec
0.020 - 0.040 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 39.0 MPa
5660 psi
5 mm/min; ISO 527
41.0 MPa
5950 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 14 %
14 %
Type I, 5 mm/min; ASTM D638
14 %
14 %
5 mm/min; ISO 527
Elongation at Yield 8.5 %
8.5 %
Type I, 5 mm/min; ASTM D638
8.8 %
8.8 %
5 mm/min; ISO 527
Tensile Modulus 2.59 GPa
376 ksi
1 mm/min; ISO 527
2.86 GPa
415 ksi
5 mm/min; ASTM D638
Flexural Strength 62.0 MPa
8990 psi
ISO 178
Flexural Modulus 2.42 GPa
351 ksi
2 mm/min; ISO 178
2.43 GPa
352 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.360 J/cm
0.674 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.67 J/cm
6.88 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 26.0 kJ/m²
12.4 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 5.00 J

@Temperature 23.0 °C
3.69 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.23
0.23
ASTM D3702 Modified
Coefficient of Friction, Static 0.16
0.16
ASTM D3702 Modified
K (wear) Factor 16.1 x 10-8 mm³/N-M
8.00 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 99.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
55.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 104 µm/m-°C

@Temperature -30.0 - 30.0 °C
57.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 147 °C
297 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
155 °C

@Thickness 3.20 mm
311 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C
183 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
94.0 °C

@Thickness 3.20 mm
201 °F

@Thickness 0.126 in
unannealed; ASTM D648