SABIC Innovative Plastics LNP LUBRICOMP KP004XXP Acetal Copolymer

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP KP004XXP Acetal Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* KP004XXP is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ASTM D792
1.48 g/cc
0.0535 lb/in³
ISO 1183
Moisture Absorption 0.180 %
0.180 %
50% RH, 24 hrs; ASTM D570
0.430 %
0.430 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.021 - 0.029 cm/cm

@Time 86400 sec
 0.021 - 0.029 in/in

@Time 24.0 hour
 ASTM D955
0.0209 - 0.0292 cm/cm

@Time 86400 sec
 0.0209 - 0.0292 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.021 - 0.029 cm/cm

@Time 86400 sec
 0.021 - 0.029 in/in

@Time 24.0 hour
 ASTM D955
0.0209 - 0.0292 cm/cm

@Time 86400 sec
 0.0209 - 0.0292 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 39.0 MPa
5660 psi
ISO 527
43.0 MPa
6240 psi
ASTM D638
Tensile Strength, Yield 39.0 MPa
5660 psi
ISO 527
43.0 MPa
6240 psi
ASTM D638
Elongation at Break 30.3 %
30.3 %
ASTM D638
42.8 %
42.8 %
ISO 527
Elongation at Yield 13.7 %
13.7 %
ASTM D638
21.5 %
21.5 %
ISO 527
Tensile Modulus 1.83 GPa
265 ksi
50 mm/min; ASTM D638
2.02 GPa
293 ksi
1 mm/min; ISO 527
Flexural Strength 60.0 MPa
8700 psi
ISO 178
63.0 MPa
9140 psi
ASTM D790
Flexural Modulus 2.02 GPa
293 ksi
ASTM D790
2.08 GPa
302 ksi
ISO 178
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.19 J/cm
11.6 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 42.0 kJ/m²
20.0 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 3.00 J
2.21 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.25
0.25
ASTM D3702 Modified
Coefficient of Friction, Static 0.14
0.14
ASTM D3702 Modified
K (wear) Factor 18.1 x 10-8 mm³/N-M
9.00 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 111 µm/m-°C

@Temperature -40.0 - 40.0 °C
 61.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
111 µm/m-°C

@Temperature -40.0 - 40.0 °C
 61.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 114 µm/m-°C

@Temperature -40.0 - 40.0 °C
 63.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
114 µm/m-°C

@Temperature -40.0 - 40.0 °C
 63.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 79.0 °C
174 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
87.0 °C

@Thickness 3.20 mm
 189 °F

@Thickness 0.126 in
 unannealed; ASTM D648