SABIC Innovative Plastics LNP LUBRICOMP KL004U Acetal Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP KL004U Acetal Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP Lubricomp* KL004U is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. This grade was previously found under the LNP* Fulton* Tradename.
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
1.50 g/cc
0.0542 lb/in³
ASTM D792
Moisture Absorption 0.150 %
0.150 %
50% RH, 24 hrs; ASTM D570
0.260 %
0.260 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ISO 294
0.020 - 0.025 cm/cm

@Time 86400 sec
0.020 - 0.025 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0197 - 0.025 cm/cm

@Time 86400 sec
0.0197 - 0.025 in/in

@Time 24.0 hour
ISO 294
0.020 - 0.025 cm/cm

@Time 86400 sec
0.020 - 0.025 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
ISO 527
50.0 MPa
7250 psi
ASTM D638
Tensile Strength, Yield 47.0 MPa
6820 psi
ISO 527
51.0 MPa
7400 psi
ASTM D638
Elongation at Break 17.9 %
17.9 %
ASTM D638
22.7 %
22.7 %
ISO 527
Elongation at Yield 9.6 %
9.6 %
ISO 527
11.2 %
11.2 %
ASTM D638
Tensile Modulus 2.13 GPa
309 ksi
50 mm/min; ASTM D638
2.40 GPa
348 ksi
1 mm/min; ISO 527
Flexural Strength 75.0 MPa
10900 psi
ASTM D790
79.0 MPa
11500 psi
ISO 178
Flexural Modulus 2.06 GPa
299 ksi
ASTM D790
2.60 GPa
377 ksi
ISO 178
Izod Impact, Notched 0.420 J/cm
0.787 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.51 J/cm
12.2 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 45.0 kJ/m²
21.4 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 6.00 J
4.43 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Coefficient of Friction, Dynamic 0.29
0.29
ASTM D3702 Modified
Coefficient of Friction, Static 0.15
0.15
ASTM D3702 Modified
K (wear) Factor 30.2 x 10-8 mm³/N-M
15.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C

@Temperature -40.0 - 40.0 °C
61.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
110 µm/m-°C

@Temperature -40.0 - 40.0 °C
61.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 111 µm/m-°C

@Temperature -40.0 - 40.0 °C
61.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
111 µm/m-°C

@Temperature -40.0 - 40.0 °C
61.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 157 °C

@Thickness 3.20 mm
315 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
99.0 °C

@Thickness 3.20 mm
210 °F

@Thickness 0.126 in
unannealed; ASTM D648