SABIC Innovative Plastics LNP LUBRICOMP KFL34XXC Acetal Copolymer (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP KFL34XXC Acetal Copolymer (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* KFL34XXC is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.61 g/cc | 0.0582 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % @Time 86400 sec |
0.40 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 67.0 MPa | 9720 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.50 GPa | 943 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.50 GPa | 798 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.50 | 0.50 | ASTM D3702 Modified |
| K (wear) Factor | 399 x 10-8 mm³/N-M | 198 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
20.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 117 µm/m-°C @Temperature 23.0 - 60.0 °C |
65.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Halar® 500LC Polyethylene, Chlorotrifluoroethylene (ECTFE) (Unverified Data**)&
- Lehmann & Voss LUVOCOM® 1-7943 Polyamide 66, with carbon fiber, heat stabilized
- Silberline Silvex® 225-20-D
- Silikony Polskie Polsil Gum 100/60 HTV Silicone Rubber
- SABIC Innovative Plastics LNP THERMOCOMP MX85738 PP (Asia Pacific)
- Universal Wire Works 6Al-4V (ELI) (AMS 4956) Titanium Alloy Filler Metal
- ChevronTexaco Multifak® AFB NLGI Grade 2
- CP-Polymer-Technik Wellamid® 6600 TLWCP Nylon 66, Flame Protection Grade V-2, Dry
- DuPont Performance Polymers Zytel® EFE8089B BK416 Nylon 66
- C.O.I.M. LARIPUR® LPR7018 Plasticized Ester Polyurethane
Copyright © lookpolymers.com All Rights Reserved