- SABIC Innovative Plastics LNP LUBRICOMP JFL36 PES (Asia Pacific)
SABIC Innovative Plastics LNP LUBRICOMP JFL36 PES (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP JFL36 PES (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* JFL36 is a compound based on Polyethersulfone resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ASTM D792 |
| 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.290 % | 0.290 % | 50% RH, 24 hrs; ASTM D570 |
| 0.500 % | 0.500 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0040 cm/cm @Time 86400 sec |
0.0010 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ISO 527 |
| 93.0 MPa | 13500 psi | ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| 1.5 % | 1.5 % | ISO 527 | |
| Tensile Modulus | 9.54 GPa | 1380 ksi | 1 mm/min; ISO 527 |
| 12.2 GPa | 1770 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 138 MPa | 20000 psi | ISO 178 |
| 143 MPa | 20700 psi | ASTM D790 | |
| Flexural Modulus | 10.27 GPa | 1490 ksi | ASTM D790 |
| 10.84 GPa | 1572 ksi | ISO 178 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.63 J/cm | 6.80 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J | 6.64 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.36 | 0.36 | ASTM D3702 Modified |
| K (wear) Factor | 121 x 10-8 mm³/N-M | 60.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 22.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 35.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 35.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 |