SABIC Innovative Plastics LNP LUBRICOMP IFL34 PA 6/12 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 612
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP IFL34 PA 6/12 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* IFL34 is a compound based on Nylon 6/12 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ASTM D792
1.35 g/cc
0.0488 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ASTM D955
0.0041 cm/cm

@Time 86400 sec
0.0041 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.010 - 0.012 cm/cm

@Time 86400 sec
0.010 - 0.012 in/in

@Time 24.0 hour
ASTM D955
0.011 cm/cm

@Time 86400 sec
0.011 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 115 MPa
16700 psi
ASTM D638
121 MPa
17500 psi
ISO 527
Tensile Strength, Yield 115 MPa
16700 psi
ASTM D638
121 MPa
17500 psi
ISO 527
Elongation at Break 3.0 %
3.0 %
ISO 527
3.1 %
3.1 %
ASTM D638
Elongation at Yield 3.0 %
3.0 %
ISO 527
3.1 %
3.1 %
ASTM D638
Tensile Modulus 6.89 GPa
999 ksi
50 mm/min; ASTM D638
7.10 GPa
1030 ksi
1 mm/min; ISO 527
Flexural Strength 172 MPa
24900 psi
ASTM D790
176 MPa
25500 psi
ISO 178
Flexural Modulus 5.51 GPa
799 ksi
ASTM D790
6.10 GPa
885 ksi
ISO 178
Izod Impact, Notched 0.960 J/cm
1.80 ft-lb/in
ASTM D256
Izod Impact, Unnotched 9.29 J/cm
17.4 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 53.0 kJ/m²
25.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 8.00 J
5.90 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.46
0.46
ASTM D3702 Modified
Coefficient of Friction, Static 0.47
0.47
ASTM D3702 Modified
K (wear) Factor 36.3 x 10-8 mm³/N-M
18.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 99.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
55.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
99.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
55.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 39.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
21.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
39.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
22.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 212 °C
414 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
212 °C

@Thickness 3.20 mm
414 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 195 °C
383 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
197 °C

@Thickness 3.20 mm
387 °F

@Thickness 0.126 in
unannealed; ASTM D648