SABIC Innovative Plastics LNP LUBRICOMP HFG25Z PA 11

Category Polymer , Thermoplastic , Nylon , Nylon 11
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP HFG25Z PA 11.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* HFG25Z is a compound based on Nylon 11 resin containing 25% Glass Fiber, 10% Graphite. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.30 g/cc
0.0470 lb/in³
ASTM D792
1.30 g/cc
0.0470 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0047 cm/cm

@Time 86400 sec
0.0047 in/in

@Time 24.0 hour
ISO 294
0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm

@Time 86400 sec
0.0080 - 0.010 in/in

@Time 24.0 hour
ASTM D955
0.0093 cm/cm

@Time 86400 sec
0.0093 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 76.0 MPa
11000 psi
ISO 527
152 MPa
22000 psi
ASTM D638
Tensile Strength, Yield 76.0 MPa
11000 psi
ISO 527
152 MPa
22000 psi
ASTM D638
Elongation at Break 2.3 %
2.3 %
ISO 527
2.7 %
2.7 %
ASTM D638
Elongation at Yield 2.2 %
2.2 %
ISO 527
2.7 %
2.7 %
ASTM D638
Tensile Modulus 6.83 GPa
991 ksi
1 mm/min; ISO 527
11.03 GPa
1600 ksi
50 mm/min; ASTM D638
Flexural Strength 96.0 MPa
13900 psi
ASTM D790
352 MPa
51100 psi
ISO 178
Flexural Modulus 5.51 GPa
799 ksi
ASTM D790
18.2 GPa
2640 ksi
ISO 178
Izod Impact, Notched 0.690 J/cm
1.29 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.53 J/cm
8.49 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 29.0 kJ/m²
13.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 15.0 J
11.1 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.41
0.41
ASTM D3702 Modified
Coefficient of Friction, Static 0.45
0.45
ASTM D3702 Modified
K (wear) Factor 117 x 10-8 mm³/N-M
58.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 91.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
92.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 34.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
19.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
35.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
19.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 182 °C
360 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
182 °C

@Thickness 3.20 mm
360 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 166 °C
331 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
171 °C

@Thickness 3.20 mm
340 °F

@Thickness 0.126 in
unannealed; ASTM D648