SABIC Innovative Plastics LNP LUBRICOMP FL004 PE (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP FL004 PE (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* FL004 is a compound based on Polyethylene resin containing PTFE.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.024 - 0.028 cm/cm
0.024 - 0.028 in/in
on Tensile Bar; SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 21.0 MPa
3050 psi
50 mm/min; ISO 527
Elongation at Yield 8.3 %
8.3 %
50 mm/min; ISO 527
Tensile Modulus 0.900 GPa
131 ksi
1 mm/min; ISO 527
Flexural Yield Strength 21.0 MPa
3050 psi
2 mm/min; ISO 178
Flexural Modulus 0.800 GPa
116 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 174 µm/m-°C

@Temperature 23.0 - 60.0 °C
 96.7 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 152 µm/m-°C

@Temperature 23.0 - 60.0 °C
 84.4 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 47.0 °C
117 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af