SABIC Innovative Plastics LNP LUBRICOMP EX06405 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP EX06405 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* EX06405 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 |
| 1.53 g/cc | 0.0553 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0042 cm/cm @Time 86400 sec |
0.0042 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0051 cm/cm @Time 86400 sec |
0.0051 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 119 MPa | 17300 psi | ISO 527 |
| 122 MPa | 17700 psi | ASTM D638 | |
| Tensile Strength, Yield | 119 MPa | 17300 psi | ISO 527 |
| 122 MPa | 17700 psi | ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| 2.4 % | 2.4 % | ISO 527 | |
| Elongation at Yield | 2.4 % | 2.4 % | ASTM D638 |
| 2.4 % | 2.4 % | ISO 527 | |
| Tensile Modulus | 7.14 GPa | 1040 ksi | 1 mm/min; ISO 527 |
| 7.58 GPa | 1100 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 151 MPa | 21900 psi | ASTM D790 |
| 169 MPa | 24500 psi | ISO 178 | |
| Flexural Modulus | 6.89 GPa | 999 ksi | ASTM D790 |
| 6.90 GPa | 1000 ksi | ISO 178 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.91 J/cm | 9.20 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.43 | 0.43 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.51 | 0.51 | ASTM D3702 Modified |
| K (wear) Factor | 139 x 10-8 mm³/N-M | 69.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
19.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 36.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 37.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 211 °C | 412 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 208 °C @Thickness 3.20 mm |
406 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 202 °C @Thickness 3.20 mm |
396 °F @Thickness 0.126 in |
unannealed; ASTM D648 |