SABIC Innovative Plastics LNP LUBRICOMP EP003 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP EP003 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp EP003 is a Polyetherimide containing 15% PTFE/Silicone. Added features include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.190 % | 0.190 % | 50% RH, 24 hrs; ASTM D570 |
| 0.260 % | 0.260 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 76.0 MPa | 11000 psi | Type I, 5 mm/min; ASTM D638 |
| 77.0 MPa | 11200 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 |
| 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 8.9 % | 8.9 % | 5 mm/min; ISO 527 |
| 17 % | 17 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 6.5 % | 6.5 % | 5 mm/min; ISO 527 |
| 6.6 % | 6.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.74 GPa | 397 ksi | 1 mm/min; ISO 527 |
| 2.79 GPa | 405 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 92.0 MPa | 13300 psi | ISO 178 |
| Flexural Modulus | 2.63 GPa | 381 ksi | 2 mm/min; ISO 178 |
| 2.83 GPa | 410 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.660 J/cm | 1.24 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.63 J/cm | 12.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.22 | 0.22 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.13 | 0.13 | ASTM D3702 Modified |
| K (wear) Factor | 52.4 x 10-8 mm³/N-M | 26.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
27.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 51.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
28.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 189 °C | 372 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 193 °C @Thickness 3.20 mm |
379 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CP8320 PC+ABS
- Samsung Cheil Industries Infino® VB-5300G PBT, Glass Filled FR
- Solvay GEROPON® SC/213 Surfactant
- Universal Wire Works 70S-2 Steel Welding Wire
- 3M 9456 Double Coated Tapes with Adhesive 340
- BASF Ultramid® C3U10 PA6/66 FR (Dry)
- Ametek High Purity Nickel Strip 899M Hard
- Materion ToughMet® T3 AT110 (OD
- Henkel Hysol EA 9396/C-2 Paste Adhesive System
Copyright © lookpolymers.com All Rights Reserved