SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP EL003 PEI (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* EL003 is a compound based on Polyetherimide resin containing PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ASTM D792
1.35 g/cc
0.0488 lb/in³
ISO 1183
Moisture Absorption 0.210 %
0.210 %
50% RH, 24 hrs; ASTM D570
0.250 %
0.250 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0080 - 0.011 cm/cm

@Time 86400 sec
0.0080 - 0.011 in/in

@Time 24.0 hour
ASTM D955
0.0080 - 0.011 cm/cm

@Time 86400 sec
0.0080 - 0.011 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0080 - 0.011 cm/cm

@Time 86400 sec
0.0080 - 0.011 in/in

@Time 24.0 hour
ASTM D955
0.0080 - 0.011 cm/cm

@Time 86400 sec
0.0080 - 0.011 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 82.0 MPa
11900 psi
ISO 527
85.0 MPa
12300 psi
ASTM D638
Tensile Strength, Yield 83.0 MPa
12000 psi
ISO 527
88.0 MPa
12800 psi
ASTM D638
Elongation at Break 8.1 %
8.1 %
ISO 527
10.3 %
10.3 %
ASTM D638
Elongation at Yield 6.3 %
6.3 %
ISO 527
6.5 %
6.5 %
ASTM D638
Tensile Modulus 2.74 GPa
397 ksi
1 mm/min; ISO 527
2.75 GPa
399 ksi
50 mm/min; ASTM D638
Flexural Strength 130 MPa
18900 psi
ISO 178
135 MPa
19600 psi
ASTM D790
Flexural Modulus 2.89 GPa
419 ksi
ASTM D790
3.02 GPa
438 ksi
ISO 178
Izod Impact, Notched 0.690 J/cm
1.29 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.47 J/cm
14.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 61.0 kJ/m²
29.0 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 9.00 J
6.64 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.30
0.30
ASTM D3702 Modified
Coefficient of Friction, Static 0.23
0.23
ASTM D3702 Modified
K (wear) Factor 214 x 10-8 mm³/N-M
106 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 47.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.5 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
47.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 47.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
47.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 182 °C
360 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
182 °C

@Thickness 3.20 mm
360 °F

@Thickness 0.126 in
unannealed; ASTM D648