SABIC Innovative Plastics LNP LUBRICOMP DX94375H PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DX94375H PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* DX94375H is a compound based on Polycarbonate resin containing Proprietary Fillers. Added features of this material include: Healthcare, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ASTM D955 |
| 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 43.0 MPa | 6240 psi | ISO 527 |
| 44.0 MPa | 6380 psi | ASTM D638 | |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | ISO 527 |
| 52.0 MPa | 7540 psi | ASTM D638 | |
| Elongation at Break | 5.6 % | 5.6 % | ASTM D638 |
| 52 % | 52 % | ISO 527 | |
| Elongation at Yield | 5.1 % | 5.1 % | ISO 527 |
| 5.7 % | 5.7 % | ASTM D638 | |
| Tensile Modulus | 1.86 GPa | 270 ksi | 50 mm/min; ASTM D638 |
| 2.10 GPa | 305 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 68.0 MPa | 9860 psi | ASTM D790 |
| 81.0 MPa | 11700 psi | ISO 178 | |
| Flexural Modulus | 2.04 GPa | 296 ksi | ASTM D790 |
| 2.30 GPa | 334 ksi | ISO 178 | |
| Izod Impact, Notched | 1.49 J/cm | 2.79 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 137 kJ/m² | 65.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 33.0 J | 24.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 128 °C @Thickness 3.20 mm |
262 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Edgetek® NN-40CF/000 FRV0 NATURAL Polyamide 66 (Nylon 66)
- Indium Corp. Indalloy 16 Low Melting Bismuth Alloy
- Industeel SUPERELSO® 500HR Quenched and Tempered High Strength Steel for Wet H2S Service
- SABIC Innovative Plastics PC0700 PC (Asia Pacific)
- Samsung Cheil Industries Starex® HR-1360 HIPS, Unreinforced Heat Resistant
- SABIC Innovative Plastics LNP STAT-KON EEF42 PEI (Asia Pacific)
- Westlake Tymax™ GT4524 Anhydride Modified Linear Low Density Polyethylene
- A. Schulman LP552-01 Injection Molding, Extrusion Grade Compound
- Tra-Con Tra-Bond 526M05 Rapid Low Temperature Cure Adhesive
- CPC - Vycom FLAMETEC™ CP7-D Flame Retardant Polypropylene
Copyright © lookpolymers.com All Rights Reserved