SABIC Innovative Plastics LNP LUBRICOMP DP003 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DP003 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* DP003 is a compound based on Polycarbonate resin containing 15% PTFE/Silicone. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 |
| 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.190 % | 0.190 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ISO 294 |
| 0.0090 - 0.010 cm/cm @Time 86400 sec |
0.0090 - 0.010 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ASTM D955 |
| 0.010 - 0.012 cm/cm @Time 86400 sec |
0.010 - 0.012 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527 |
| 42.0 MPa | 6090 psi | ASTM D638 | |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | ASTM D638 |
| 49.0 MPa | 7110 psi | ISO 527 | |
| Elongation at Break | 35.1 % | 35.1 % | ASTM D638 |
| 41.2 % | 41.2 % | ISO 527 | |
| Elongation at Yield | 5.6 % | 5.6 % | ASTM D638 |
| 5.8 % | 5.8 % | ISO 527 | |
| Tensile Modulus | 2.16 GPa | 313 ksi | 1 mm/min; ISO 527 |
| 2.23 GPa | 323 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 75.0 MPa | 10900 psi | ASTM D790 |
| 75.0 MPa | 10900 psi | ISO 178 | |
| Flexural Modulus | 1.84 GPa | 267 ksi | ISO 178 |
| 1.89 GPa | 274 ksi | ASTM D790 | |
| Izod Impact, Notched | 2.83 J/cm | 5.30 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 31.0 kJ/m² | 14.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 28.0 J | 20.7 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 61.0 J | 45.0 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.10 | 0.10 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.26 | 0.26 | ASTM D3702 Modified |
| K (wear) Factor | 84.6 x 10-8 mm³/N-M | 42.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 66.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 67.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 71.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
39.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D648 |