SABIC Innovative Plastics LNP LUBRICOMP DL004 PC (Asia Pacific)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP DL004 PC (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Lubricomp* DL004 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated.

Physical Properties	Metric	English	Comments
Density	1.30 g/cc	0.0470 lb/inÂ³	ASTM D792
	1.30 g/cc	0.0470 lb/inÂ³	ISO 1183
Moisture Absorption	0.200 %	0.200 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0059 cm/cm @Time 86400 sec	0.0059 in/in @Time 24.0 hour	ISO 294
	0.0060 cm/cm @Time 86400 sec	0.0060 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0060 cm/cm @Time 86400 sec	0.0060 in/in @Time 24.0 hour	ASTM D955
	0.0064 cm/cm @Time 86400 sec	0.0064 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	38.0 MPa	5510 psi	ASTM D638
	39.0 MPa	5660 psi	ISO 527
Tensile Strength, Yield	42.0 MPa	6090 psi	ASTM D638
	44.0 MPa	6380 psi	ISO 527
Elongation at Break	28.9 %	28.9 %	ASTM D638
	29.3 %	29.3 %	ISO 527
Elongation at Yield	5.9 %	5.9 %	ISO 527
	6.1 %	6.1 %	ASTM D638
Tensile Modulus	2.05 GPa	297 ksi	1 mm/min; ISO 527
	2.06 GPa	299 ksi	50 mm/min; ASTM D638
Flexural Strength	63.0 MPa	9140 psi	ISO 178
	73.0 MPa	10600 psi	ASTM D790
Flexural Modulus	2.00 GPa	290 ksi	ISO 178
	2.06 GPa	299 ksi	ASTM D790
Izod Impact, Notched	1.06 J/cm	1.99 ft-lb/in	ASTM D256
Izod Impact, Unnotched	18.69 J/cm	35.01 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	11.0 kJ/mÂ²	5.23 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	178 kJ/mÂ²	84.7 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	24.0 J	17.7 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	21.0 J	15.5 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.34	0.34	ASTM D3702 Modified
Coefficient of Friction, Static	0.19	0.19	ASTM D3702 Modified
K (wear) Factor	14.1 x 10^-8 mmÂ³/N-M	7.00 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	77.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	42.8 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	77.4 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	43.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
CTE, linear, Transverse to Flow	75.6 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	42.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	76.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	42.2 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	143 Â°C	289 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	141 Â°C @Thickness 3.20 mm	286 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	129 Â°C	264 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	127 Â°C @Thickness 3.20 mm	261 Â°F @Thickness 0.126 in	unannealed; ASTM D648