SABIC Innovative Plastics LNP LUBRICOMP DL003EXJ PC

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP DL003EXJ PC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Lubricomp* DL003EXJ is a compound based on Polycarbonate containing 15% PTFE. Characteristics of this grade are Easy Molding, Low Extractable, Internally Lubricated, Healthcare.

Physical Properties	Metric	English	Comments
Specific Gravity	1.29 g/cc	1.29 g/cc	ASTM D792
Density	1.29 g/cc	0.0466 lb/inÂ³	ASTM D792
Moisture Absorption	0.100 %	0.100 %	50% RH, 24 hrs; ASTM D570
	0.150 %	0.150 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.0060 - 0.0080 cm/cm @Time 86400 sec	0.0060 - 0.0080 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	34.0 MPa	4930 psi	5 mm/min; ISO 527
	38.0 MPa	5510 psi	Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield	45.0 MPa	6530 psi	5 mm/min; ISO 527
	46.0 MPa	6670 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	17.3 %	17.3 %	Type I, 5 mm/min; ASTM D638
	21.8 %	21.8 %	5 mm/min; ISO 527
Elongation at Yield	5.4 %	5.4 %	5 mm/min; ISO 527
	5.6 %	5.6 %	Type I, 5 mm/min; ASTM D638
Tensile Modulus	1.98 GPa	287 ksi	1 mm/min; ISO 527
	2.09 GPa	303 ksi	50 mm/min; ASTM D638
Flexural Strength	67.0 MPa	9720 psi	ISO 178
Flexural Modulus	2.00 GPa	290 ksi	2 mm/min; ISO 178
	2.19 GPa	318 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	1.76 J/cm	3.30 ft-lb/in	ASTM D256
Izod Impact, Unnotched	17.8 J/cm	33.3 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	12.0 kJ/mÂ²	5.71 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	110 kJ/mÂ²	52.3 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	33.0 J @Temperature 23.0 Â°C	24.3 ft-lb @Temperature 73.4 Â°F	ASTM D3763
Impact Test	28.0 J	20.7 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.38	0.38	ASTM D3702 Modified
Coefficient of Friction, Static	0.23	0.23	ASTM D3702 Modified
K (wear) Factor	30.2 x 10^-8 mmÂ³/N-M	15.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	77.0 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	42.8 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
CTE, linear, Transverse to Flow	77.0 Âµm/m-Â°C @Temperature -30.0 - 30.0 Â°C	42.8 Âµin/in-Â°F @Temperature -22.0 - 86.0 Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	141 Â°C	286 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	141 Â°C @Thickness 3.20 mm	286 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	124 Â°C	255 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	130 Â°C @Thickness 3.20 mm	266 Â°F @Thickness 0.126 in	unannealed; ASTM D648