SABIC Innovative Plastics LNP LUBRICOMP DL0039EF PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DL0039EF PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DL-0039EF is a compound based on Polycarbonate resin containing 15% PTFE. Characteristics of this grade include: Flame Retardant and Internally Lubricated.
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D792
Density 1.30 g/cc
0.0470 lb/in³
ASTM D792
Moisture Absorption 0.110 %
0.110 %
50% RH, 24 hrs; ASTM D570
0.180 %
0.180 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.0 MPa
6380 psi
Type I, 5 mm/min; ASTM D638
44.0 MPa
6380 psi
5 mm/min; ISO 527
Tensile Strength, Yield 52.0 MPa
7540 psi
5 mm/min; ISO 527
53.0 MPa
7690 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 22 %
22 %
Type I, 5 mm/min; ASTM D638
27 %
27 %
5 mm/min; ISO 527
Elongation at Yield 5.4 %
5.4 %
Type I, 5 mm/min; ASTM D638
5.5 %
5.5 %
5 mm/min; ISO 527
Tensile Modulus 2.09 GPa
303 ksi
1 mm/min; ISO 527
2.21 GPa
321 ksi
5 mm/min; ASTM D638
Flexural Strength 77.0 MPa
11200 psi
ISO 178
Flexural Modulus 2.09 GPa
303 ksi
2 mm/min; ISO 178
2.24 GPa
325 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched (ISO) 142 kJ/m²
67.6 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 1740 kJ/m²
828 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 36.0 J

@Temperature 23.0 °C
26.6 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 35.0 J
25.8 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.35
0.35
ASTM D3702 Modified
Coefficient of Friction, Static 0.18
0.18
ASTM D3702 Modified
K (wear) Factor 12.1 x 10-8 mm³/N-M
6.00 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 75.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
41.7 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 76.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
42.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 137 °C
279 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
137 °C

@Thickness 3.20 mm
279 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 125 °C
257 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
126 °C

@Thickness 3.20 mm
259 °F

@Thickness 0.126 in
unannealed; ASTM D648