SABIC Innovative Plastics LNP LUBRICOMP DL002P PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DL002P PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* DL002P is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Exceptional Processing, Internally Lubricated.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792
1.25 g/cc
0.0452 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
0.200 %
0.200 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D955
0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.010 - 0.012 cm/cm

@Time 86400 sec
0.010 - 0.012 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 43.0 MPa
6240 psi
ISO 527
44.0 MPa
6380 psi
ASTM D638
Tensile Strength, Yield 53.0 MPa
7690 psi
ASTM D638
54.0 MPa
7830 psi
ISO 527
Elongation at Break 23.1 %
23.1 %
ISO 527
30.5 %
30.5 %
ASTM D638
Elongation at Yield 5.3 %
5.3 %
ASTM D638
5.6 %
5.6 %
ISO 527
Tensile Modulus 2.45 GPa
355 ksi
50 mm/min; ASTM D638
2.46 GPa
357 ksi
1 mm/min; ISO 527
Flexural Strength 82.0 MPa
11900 psi
ASTM D790
85.0 MPa
12300 psi
ISO 178
Flexural Modulus 2.07 GPa
300 ksi
ISO 178
2.20 GPa
319 ksi
ASTM D790
Izod Impact, Notched 1.06 J/cm
1.99 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
Dart Drop, Total Energy 34.0 J
25.1 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 74.0 J
54.6 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.28
0.28
ASTM D3702 Modified
Coefficient of Friction, Static 0.17
0.17
ASTM D3702 Modified
K (wear) Factor 195 x 10-8 mm³/N-M
97.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 66.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
37.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
66.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
37.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
73.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 123 °C
253 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
120 °C

@Thickness 3.20 mm
248 °F

@Thickness 0.126 in
unannealed; ASTM D648