SABIC Innovative Plastics LNP LUBRICOMP DL002F PC

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP DL002F PC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP LUBRICOMP* DL002F is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Internally Lubricated, Superior Molding.

Physical Properties	Metric	English	Comments
Density	1.25 g/cc	0.0452 lb/in³	ASTM D792
Linear Mold Shrinkage, Flow	0.0060 - 0.0090 cm/cm @Time 86400 sec	0.0060 - 0.0090 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0060 - 0.010 cm/cm @Time 86400 sec	0.0060 - 0.010 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	48.0 MPa	6960 psi	ASTM D638
Tensile Strength, Yield	55.0 MPa	7980 psi	ASTM D638
Elongation at Break	19 %	19 %	ASTM D638
Elongation at Yield	4.6 %	4.6 %	ASTM D638
Flexural Strength	87.0 MPa	12600 psi	ASTM D790
Flexural Modulus	2.28 GPa	331 ksi	ASTM D790
Izod Impact, Notched	1.10 J/cm	2.06 ft-lb/in	ASTM D256
Izod Impact, Unnotched	NB	NB	ASTM D4812

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	124 °C @Thickness 3.20 mm	255 °F @Thickness 0.126 in	unannealed; ASTM D648