SABIC Innovative Plastics LNP LUBRICOMP DL002 PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DL002 PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* DL002 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0070 - 0.0090 cm/cm

@Time 86400 sec
 0.0070 - 0.0090 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm

@Time 86400 sec
 0.0070 - 0.0090 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
ASTM D638
Elongation at Break 53 %
53 %
ASTM D638
Flexural Strength 81.0 MPa
11700 psi
ASTM D790
Flexural Modulus 2.27 GPa
329 ksi
ASTM D790
Izod Impact, Notched 2.40 J/cm
4.50 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Coefficient of Friction, Dynamic 0.28
0.28
ASTM D3702 Modified
Coefficient of Friction, Static 0.17
0.17
ASTM D3702 Modified
K (wear) Factor 195 x 10-8 mm³/N-M
97.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 128 °C

@Thickness 3.20 mm
 262 °F

@Thickness 0.126 in
 unannealed; ASTM D648