SABIC Innovative Plastics LNP LUBRICOMP DL001 PC

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP DL001 PC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* DL001 is a compound based on Polycarbonate resin containing 5% PTFE. Added features of this material include: Internally Lubricated.

Physical Properties	Metric	English	Comments
Density	1.22 g/cc	0.0441 lb/in³	ASTM D792
	1.22 g/cc	0.0441 lb/in³	ISO 1183
Moisture Absorption	0.100 %	0.100 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0078 cm/cm @Time 86400 sec	0.0078 in/in @Time 24.0 hour	ISO 294
	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0096 cm/cm @Time 86400 sec	0.0096 in/in @Time 24.0 hour	ISO 294
	0.0090 - 0.011 cm/cm @Time 86400 sec	0.0090 - 0.011 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	51.0 MPa	7400 psi	ASTM D638
	53.0 MPa	7690 psi	ISO 527
Tensile Strength, Yield	54.0 MPa	7830 psi	ISO 527
	56.0 MPa	8120 psi	ASTM D638
Elongation at Break	76.6 %	76.6 %	ASTM D638
	167 %	167 %	ISO 527
Elongation at Yield	6.0 %	6.0 %	ISO 527
	6.2 %	6.2 %	ASTM D638
Tensile Modulus	2.06 GPa	299 ksi	50 mm/min; ASTM D638
	2.19 GPa	318 ksi	1 mm/min; ISO 527
Flexural Strength	70.0 MPa	10200 psi	ISO 178
Flexural Modulus	2.06 GPa	299 ksi	ASTM D790
	2.10 GPa	305 ksi	ISO 178
Izod Impact, Notched	1.60 J/cm	3.00 ft-lb/in	ASTM D256
Izod Impact, Unnotched	24.19 J/cm	45.32 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	12.0 kJ/m²	5.71 ft-lb/in²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	176 kJ/m²	83.7 ft-lb/in²	80104; ISO 180/1U
Dart Drop, Total Energy	39.0 J	28.8 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	49.0 J	36.1 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.39	0.39	ASTM D3702 Modified
Coefficient of Friction, Static	0.32	0.32	ASTM D3702 Modified
K (wear) Factor	183 x 10^-8 mm³/N-M	91.0 x 10^-10 in³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	73.8 µm/m-°C @Temperature -40.0 - 40.0 °C	41.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	74.0 µm/m-°C @Temperature -40.0 - 40.0 °C	41.1 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
CTE, linear, Transverse to Flow	75.6 µm/m-°C @Temperature -40.0 - 40.0 °C	42.0 µin/in-°F @Temperature -40.0 - 104 °F	ASTM E 831
	76.0 µm/m-°C @Temperature -40.0 - 40.0 °C	42.2 µin/in-°F @Temperature -40.0 - 104 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	142 °C	288 °F	Flatw 80104 sp=64mm; ISO 75/Bf
	142 °C @Thickness 3.20 mm	288 °F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	129 °C	264 °F	Flatw 80104 sp=64mm; ISO 75/Af
	132 °C @Thickness 3.20 mm	270 °F @Thickness 0.126 in	unannealed; ASTM D648