SABIC Innovative Plastics LNP LUBRICOMP DFP34 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DFP34 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* DFP34 is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0036 cm/cm @Time 86400 sec |
0.0036 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0044 cm/cm @Time 86400 sec |
0.0044 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 103 MPa | 14900 psi | ASTM D638 |
| 104 MPa | 15100 psi | ISO 527 | |
| Tensile Strength, Yield | 103 MPa | 14900 psi | ASTM D638 |
| 103 MPa | 14900 psi | ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| 2.8 % | 2.8 % | ASTM D638 | |
| Elongation at Yield | 2.5 % | 2.5 % | ISO 527 |
| 2.8 % | 2.8 % | ASTM D638 | |
| Tensile Modulus | 6.74 GPa | 978 ksi | 1 mm/min; ISO 527 |
| 6.89 GPa | 999 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 158 MPa | 22900 psi | ASTM D790 |
| 158 MPa | 22900 psi | ISO 178 | |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
| 6.40 GPa | 928 ksi | ISO 178 | |
| Izod Impact, Notched | 1.38 J/cm | 2.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.20 J/cm | 13.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 44.0 kJ/m² | 20.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 24.0 J | 17.7 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.51 | 0.51 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.53 | 0.53 | ASTM D3702 Modified |
| K (wear) Factor | 218 x 10-8 mm³/N-M | 108 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 47.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 36.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 36.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |