SABIC Innovative Plastics LNP LUBRICOMP DFL36XXJ PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DFL36XXJ PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Lubricomp* DFL36XXJ is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractable, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ASTM D792 |
| 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0021 cm/cm @Time 86400 sec |
0.0021 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0071 cm/cm @Time 86400 sec |
0.0071 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 112 MPa | 16200 psi | ASTM D638 |
| 113 MPa | 16400 psi | ISO 527 | |
| Tensile Strength, Yield | 113 MPa | 16400 psi | ASTM D638 |
| 114 MPa | 16500 psi | ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| 2.6 % | 2.6 % | ISO 527 | |
| Elongation at Yield | 2.4 % | 2.4 % | ASTM D638 |
| 2.4 % | 2.4 % | ISO 527 | |
| Tensile Modulus | 9.28 GPa | 1350 ksi | 1 mm/min; ISO 527 |
| 9.65 GPa | 1400 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
| 180 MPa | 26100 psi | ISO 178 | |
| Flexural Modulus | 8.70 GPa | 1260 ksi | ISO 178 |
| 8.96 GPa | 1300 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.76 J/cm | 3.30 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² | 8.09 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 51.0 kJ/m² | 24.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 21.0 J | 15.5 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 7.00 J | 5.16 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.57 | 0.57 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.49 | 0.49 | ASTM D3702 Modified |
| K (wear) Factor | 54.4 x 10-8 mm³/N-M | 27.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 47.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 30.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 149 °C | 300 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 144 °C | 291 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |