SABIC Innovative Plastics LNP LUBRICOMP DFL36EU PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DFL36EU PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DFL36EU is a compound based on Polycarbonate resin containing 30% Glass Fiber, 15% PTFE. Added features include: Internally Lubricated, Easy Molding and UV Stabilized.
Physical Properties Metric English Comments
Specific Gravity 1.56 g/cc
1.56 g/cc
ASTM D792
Density 1.56 g/cc
0.0564 lb/in³
ASTM D792
Moisture Absorption 0.0800 %
0.0800 %
50% RH, 24 hrs; ASTM D570
0.110 %
0.110 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Time 86400 sec
0.0050 - 0.0070 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 113 MPa
16400 psi
5 mm/min; ISO 527
116 MPa
16800 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.6 %
2.6 %
5 mm/min; ISO 527
2.7 %
2.7 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 8.68 GPa
1260 ksi
1 mm/min; ISO 527
9.22 GPa
1340 ksi
5 mm/min; ASTM D638
Flexural Strength 175 MPa
25400 psi
ISO 178
189 MPa
27400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 190 MPa
27600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 8.33 GPa
1210 ksi
2 mm/min; ISO 178
8.91 GPa
1290 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.68 J/cm
3.15 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.09 J/cm
13.3 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 16.0 kJ/m²
7.61 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 51.0 kJ/m²
24.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 16.0 J

@Temperature 23.0 °C
11.8 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 5.00 J
3.69 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.47
0.47
ASTM D3702 Modified
Coefficient of Friction, Static 0.51
0.51
ASTM D3702 Modified
K (wear) Factor 4.03 x 10-8 mm³/N-M
2.00 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D3702 Modified
60.4 x 10-8 mm³/N-M
30.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 54.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
30.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 43.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
23.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
146 °C

@Thickness 3.20 mm
295 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 141 °C
286 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
141 °C

@Thickness 3.20 mm
286 °F

@Thickness 0.126 in
unannealed; ASTM D648