SABIC Innovative Plastics LNP LUBRICOMP DFL34EH PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DFL34EH PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* DFL34EH is a compound based on Polycarbonate containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Easy Molding, Healthcare, Wear Resistant.
Physical Properties Metric English Comments
Specific Gravity 1.48 g/cc
1.48 g/cc
ASTM D792
Density 1.47 g/cc
0.0531 lb/in³
ASTM D792
Moisture Absorption 0.0900 %
0.0900 %
50% RH, 24 hrs; ASTM D570
0.130 %
0.130 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.00020 - 0.00040 cm/cm

@Time 86400 sec
0.00020 - 0.00040 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0020 - 0.0040 cm/cm

@Time 86400 sec
0.0020 - 0.0040 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 93.0 MPa
13500 psi
5 mm/min; ISO 527
95.0 MPa
13800 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.7 %
2.7 %
Type I, 5 mm/min; ASTM D638
3.1 %
3.1 %
5 mm/min; ISO 527
Elongation at Yield 2.8 %
2.8 %
5 mm/min; ISO 527
Tensile Modulus 6.65 GPa
965 ksi
1 mm/min; ISO 527
7.19 GPa
1040 ksi
50 mm/min; ASTM D638
Flexural Strength 145 MPa
21000 psi
1.3 mm/min, 50 mm span; ASTM D790
150 MPa
21800 psi
ISO 178
Flexural Modulus 6.19 GPa
898 ksi
2 mm/min; ISO 178
6.32 GPa
917 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.49 J/cm
2.79 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.40 J/cm
13.9 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 48.0 kJ/m²
22.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 19.0 J

@Temperature 23.0 °C
14.0 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 6.00 J
4.43 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.46
0.46
ASTM D3702 Modified
Coefficient of Friction, Static 0.50
0.50
ASTM D3702 Modified
K (wear) Factor 26.2 x 10-8 mm³/N-M
13.0 x 10-10 in³-min/ft-lb-hr
Ring; ASTM D3702 Modified
179 x 10-8 mm³/N-M
89.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 37.4 µm/m-°C

@Temperature -30.0 - 30.0 °C
20.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 63.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
35.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 146 °C
295 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
146 °C

@Thickness 3.20 mm
295 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 141 °C
286 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
142 °C

@Thickness 3.20 mm
288 °F

@Thickness 0.126 in
unannealed; ASTM D648